Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | | ASTM D-1238 | 10 | g/10min |
| Taber wear amount | H 18轮 | ASTM D-1044 | 310 | mg/1000rev |
| Taber wear amount | CS-17轮 | ASTM D-1044 | 30 | mg/1000rev |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Initial tear resistance performance | | ASTM D-1004 | 51 | kN/m |
| Stretching force | 5%伸长 | ASTM D-638 | 1.7 | Mpa |
| Stretching force | 10%伸长 | ASTM D-638 | 2.6 | Mpa |
| Ezo impact strength | 23℃ | ASTM D-256 | 不破裂 | J/m |
| Fracture elongation | | ASTM D-638 | 200 | % |
| Rubbing modulus | 23℃ | ASTM D-790 | 32.4 | Mpa |
| Fracture tensile force | | ASTM D-638 | 10.3 | Mpa |
| Hardness tester hardness | | ASTM D-2240 | 35 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal distortion temperature | @0.5Mpa | ASTM D-648 | N/A | °C |
| Thermal distortion temperature | @0.18Mpa | ASTM D-648 | N/A | °C |
| melting point | | ASTM D-3418 | 156 | °C |
| vicat softening point | | ASTM D-1525 | 77 | °C |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Wear resistant and flexible incision growth performance | | ASTM D-1052 | >1×10 | |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| 24-hour water absorption rate | | ASTM D-570 | 5 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.