| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 9.8 | g/10min |
| Content of comonomer 3 | | 内部方法 | 8.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus -2% secant | | ASTMD638,ISO527-2 | 110 | Mpa |
| Tensile strength | 屈服 | ASTMD638,ISO527-2 | 7.00 | Mpa |
| Tensile strength | 断裂 | ASTMD638,ISO527-2 | 19.0 | Mpa |
| elongation | 断裂 | ASTMD638,ISO527-2 | 570 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | -- | ASTMD1525 | 82.2 | °C |
| Vicat softening temperature | -- | ISO306 | 82.0 | °C |
| Melting temperature (DSC) | | 内部方法 | 100 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Initial sealing temperature 4 | | 内部方法 | 85.0 | °C |
| Water vapor permeability 5 | 38°C,90%RH | DIN53122/2 | 0.40 | g·mm/m²/atm/24hr |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | 邵氏D | ASTMD2240,ISO868 | 53 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.