Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | | ASTM D-955 | 0.4～0.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strain at break | 23℃ | ASTM D-638 | 30 | % |
| IZOD notch impact strength | 1/8in(3.2mm).23℃ | ASTM D-256 | 28 | kg.cm/cm |
| tensile strength | 23℃ | ASTM D-638 | 450 | kg/cm |
| Rockwell hardness | R SCALE | ASTM D-785 | 105 | R |
| Flexural modulus of elasticity | 23℃ | ASTM D-790 | 23000 | kg/cm |
| bending strength | 23℃ | ASTM D-790 | 650 | kg/cm |
| IZOD notch impact strength | 1/4in(6.4mm).23℃ | ASTM D-256 | 25 | kg.cm/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 6.4mm 18.6kg/cm | ASTM D-648 | 95（203） | ℃（℉） |
| vicat softening point | | ASTM D-1525 | 95（203） | ℃（℉） |
| Hot deformation temperature | 6.4mm 18.6kg/cm | ASTM D-648 | 85（185） | ℃（℉） |
| Combustibility | | UL-94 | HB | CLASS |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃×5kg | ASTM D-1238 | 2.9 | g/10min |
| Density/specific gravity | 23℃ | ASTM D-792 | 1.04 | g/cm |
| Melt index | 200℃×21.6kg | ASTM D-1238 | 39 | g/10min |
| Melt index | 220℃×10kg | ASTM D-1238 | 30 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.