| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt flow rate | 200°C/5.0 kg | ASTM D1238, ISO 1133 | 2.3 | g/10 min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 23°C | ASTM D638, ISO 527-2 | 3040 | Mpa |
| Tensile strength | 23°C | ASTM D638, ISO 527-2 | 51.0 | Mpa |
| elongation | 断裂, 23°C | ASTM D638, ISO 527-2 | 2.0 | % |
| Bending modulus | 23°C | ASTM D790, ISO 178 | 3330 | Mpa |
| bending strength | 23°C | ASTM D790, ISO 178 | 98.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal deformation temperature under load | 1.8 MPa, 退火, 3.18 mm | ASTM D648, ISO 75-2/A | 95.0 | °C |
| Vicat softening temperature | | ASTM D1525, ISO 306 | 104 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 75 | °C |
| drying time | | | 1.0 到 2.0 | hr |
| Hopper temperature | | | 40 | °C |
| Temperature at the rear of the barrel | | | 195 | °C |
| Temperature in the middle of the barrel | | | 210 到 220 | °C |
| Temperature at the front of the material cylinder | | | 215 | °C |
| Processing (melt) temperature | | | 190 到 230 | °C |
| Mold temperature | | | 20 到 70 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5 mm, NC | UL 94 | HB | |
| Residual monomer | | | < 700 | ppm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.