Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.16 | |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 1.8 | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 230℃/3.8 kg | ASTM D1238 | 1.8 | g/10 min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | 屈服, 3.18 mm | ASTM D638 | 70.3 | Mpa |
| Impact strength of cantilever beam gap | 23℃, 6.35 mm | ASTM D256 | 20 | J/m |
| elongation at break | | ASTM D638/ISO 527 | 5.0 | % |
| tensile strength | | ASTM D638/ISO 527 | 70.3 | kg/cm²(MPa)[Lb/in²] |
| elongation | 断裂, 3.18 mm | ASTM D638 | 5.0 | % |
| Rockwell hardness | M 计秤, 6.35 mm | ASTM D785 | 95 | |
| Rockwell hardness | | ASTM D785 | 95 | |
| bending strength | | ASTM D790/ISO 178 | 108 | kg/cm²(MPa)[Lb/in²] |
| bending strength | 6.35 mm | ASTM D790 | 108 | Mpa |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 20 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8 MPa, 未退火, 6.35 mm | ASTM D648 | 100 | °C |
| Hot deformation temperature | | ASTM D648/ISO 75 | 100 | ℃（℉） |
| vicat softening point | | ASTM D1525/ISO R306 | 113 | ℃（℉） |
| Vicat softening temperature | | ASTM D1525 | 113 | °C |
| UL flame retardant rating | 1.59 mm | UL 94 | HB | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| transmissivity | 3180 µm | ASTM D1003 | 91.0 | % |
| Haze | 3.18 µm | ASTM D1003 | < 1.0 | % |
| Huangdu Index | 3.18 mm | ASTM D1003 | 0.50 到 1.0 | YI |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Light transmittance | | ASTM D1003/ISO 13468 | 91.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.