Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt volume flow rate | 240°C/10.0kg | ISO1133 | 30.0 | cm3/10min |
| Shrinkage rate | | ISO294-4 | 0.80 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 1.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strain | 屈服,23°C | ISO527-2 | 3.5 | % |
| Bending modulus | | ISO178 | 1800 | Mpa |
| Bending stress | | ISO178 | 62.0 | Mpa |
| Tensile modulus | | ISO527-2 | 2000 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2 | 43.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature 3 | 0.45MPa,退火 | ISO75-2/B | 85.0 | °C |
| Hot deformation temperature 3 | 1.8MPa,退火 | ISO75-2/A | 65.0 | °C |
| Vicat softening temperature | -- | ISO306/A50 | 160 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 102 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+14 | ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Relative permittivity | 1MHz | IEC60250 | 2.90 | |
| Dissipation factor | 1MHz | IEC60250 | 0.015 | |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Elongation MD | 断裂 | ISO527-3 | >50 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 无断裂 | |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 无断裂 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | | ISO2039-1 | 86.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.