Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 24 hours | ASTM D570 | 0.07 | |
| Longitudinal shrinkage rate (Flow) | flow, 1.5 | Internal | 0.4~0.6 | |
| Longitudinal shrinkage rate (Flow) | flow, 3.2 | Internal | 0.6~0.9 | |
| Shrinkage rate (Across Flow) |
xflow, 1.5- | Internal | 0.5~0.8 | |
| Shrinkage rate (Across Flow) |
xflow, 3.2 | Internal | 0.8~1.1 | |
| Bi Rong | | | 0.71 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending modulus | 1.3 mm | ASTM D790 | 4820 | Mpa |
| Bending strength fracture (brk) | 1.3 mm | ASTM D790 | 144 | Mpa |
| Tensile strength fracture (brk) | Type I, 5 | ASTM D638 | 93 | Mpa |
| Tensile elongation fracture (brk) | Type I, 5 | ASTM D638 | 5 | % |
| combustion performance | Test Condition | Test Method | Test Result | Unit |
|---|
| UL fire rating HB | 10°C/min | UL94 | 0.71 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Izod Notched at 23 ℃ (73 ℉) | | | 53 | J/m |
| Cantilever beam without notch (Izod Unnotched) 23 ℃ (73 ℉) | / | | 534 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness R | | ASTM D785 | 118 | R |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Coefficient of Linear Expansion (CLTE) Longitudinal (Flow) | -40°C to | ASTM E831 | 21.6 | E-6/°C |
| Coefficient of Linear Expansion (CLTE) Longitudinal (Flow) |
60°C to | ASTM E831 | 21.6 | E-6/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare