Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Apparent density | | | 0.60 | g/cm³ |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 7.00 | cm3/10min |
| Shrinkage rate | | ISO294-4 | 0.30to0.70 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.30 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2 | 3900 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2 | 79.0 | Mpa |
| Tensile strain | 断裂,23°C | ISO527-2 | 3.0 | % |
| Bending stress | | ISO178 | 135 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature 3 | 0.45MPa,Annealed | ISO75-2/B | 110 | °C |
| Hot deformation temperature 3 | 1.8MPa,Annealed | ISO75-2/A | 104 | °C |
| Vicat softening temperature | | ISO306/B50 | 120 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| thermal conductivity | | DIN52612 | 0.17 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | >1.0E+15 | ohms |
| Volume resistivity | | IEC60093 | 1E+16 | ohms·cm |
| Dielectric constant | 100Hz | IEC60250 | 3.00 | |
| Dissipation factor | 100Hz | IEC60250 | 5E-03 | |
| Dissipation factor | 1MHz | IEC60250 | 7E-03 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 21 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 20 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M级 | | 84 | |
| Ball pressure hardness | | ISO2039-1 | 175 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ISO489 | 1.567 | |
| transmissivity | 550nm | ASTMD1003 | >89.0 | % |
| Haze | | ASTMD1003 | <1.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.