Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1040 | |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 10 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural strength | 50mm/min | ISO 178/1993 | 80 | Mpa |
| Tensile yield strength | | ISO 572-2/1993 | 50 | Mpa |
| Flexural modulus | 2mm/min | ISO 178/1993 | 3200 | Mpa |
| Charpy impact strength | | ISO 179/1993 | 10 | KJ/m |
| elongation at break | | ASTM D638/ISO 527 | 2 | % |
| elongation | | ASTM D638/ISO 527 | 50 | % |
| elongation | 50mm/min | ISO 572-2/1993 | 2 | % |
| Bending modulus | | ASTM D790/ISO 178 | 3200 | kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 80 | kg/cm²(MPa)[Lb/in²] |
| Charpy impact strength | | ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | | ASTM D648/ISO 75 | 78 | ℃（℉） |
| Hot deformation temperature | 1.82MPa | ISO 75-2/1993 | 78 | °C |
| vicat softening point | B50/oil | ISO 306/1994 | 88 | °C |
| vicat softening point | | ASTM D1525/ISO R306 | 88 | ℃（℉） |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃/5Kg | ISO 1133/1997 | 10 | g/10min |
| density | | ISO 1183/1997 | 1040 | kg/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.