Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 2.7 | g/10min |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 27 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| tensile strength | | ASTM D638/ISO 527 | 450 | kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 20 | % |
| Rockwell hardness | | ASTM D785 | 110 | |
| Bending modulus | | ASTM D790/ISO 178 | 24000 | kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 680 | kg/cm²(MPa)[Lb/in²] |
| Tensile strength | 6mm/min | ASTM D-638 | 450 | kg/cm |
| Elongation rate | 6mm/min | ASTM D-638 | 20 | % |
| Flexural elasticity | 2.8mm/min | ASTM D-790 | 24000 | kg/cm |
| bending strength | 2.8mm/min | ASTM D-790 | 680 | kg/cm |
| Rockwell hardness | | ASTM D-785 | 110 | R scale |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 16 | kg·cm/cm(J/M)ft·lb/in |
| IZOD impact strength | 1/4" | ASTM D-256 | 16 | kg-cm/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| softening point | 1kg*50℃/hr | ASTM D-792 | 104 | °C |
| vicat softening point | | ASTM D1525/ISO R306 | 104 | ℃（℉） |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃*5kg | ASTM D-1238 | 2.7 | g/10min |
| Melt index | 220℃*10kg | ASTM D-1238 | 27 | g/10min |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Yellow index | | ASTM D-1925 | 8.5(±)1.25 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.