Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | ISO294-4 | 1.5 | % |
| Shrinkage rate | MD | ISO294-4 | 1.5 | % |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 12 | g/10min |
| MediumDensity | | | 1.19 | g/cm³ |
| Density/specific gravity | | ISO1183 | 1.39 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal tensile fracture strain | | ISO527-2 | 28 | % |
| Tensile stress | 屈服 | ISO527-2 | 54.0 | Mpa |
| Tensile strain | 屈服 | ISO527-2 | 17 | % |
| Bending stress | 3.5%应变 | ISO178 | 60.0 | Mpa |
| Tensile modulus | | ISO527-2 | 2300 | Mpa |
| Bending modulus | | ISO178 | 2000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 146 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 76.0 | °C |
| Melting temperature 2 | | ISO11357-3 | 178 | °C |
| AnnealingTemperature | | | 160 | °C |
| AnnealingTime-Optional | | | 30.0 | min/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 13 | kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 9.0 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 12 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 0.75mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| FMVSS flammability | | FMVSS302 | B | |
| Fogging-G-value | condensate | ISO6452 | 2E-04 | g |
| Burning rate 3 | 1.00mm | ISO3795 | 55 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| Emission | | VDA275 | <8.00 | mg/kg |
| EmissionofOrganicCompounds | | VDA277 | 3.40 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.