Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | ISO294-4 | 0.74 | % |
| Shrinkage rate | MD | ISO294-4 | 0.70 | % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.80 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.30 | % |
| Melt volume flow rate | 360°C/10.0kg | ISO1133 | 40.0 | cm3/10min |
| Density/specific gravity | | ISO1183 | 1.23 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 23°C | ISO527-2 | 2550 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2 | 75.0 | Mpa |
| Tensile strain | 屈服,23°C | ISO527-2 | 6.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| RTIElec | 1.6mm | UL746 | 155 | °C |
| RTIElec | 3.0mm | UL746 | 155 | °C |
| Evolution Calendar intelligent importer | 1.6mm | UL746 | 130 | °C |
| Evolution Calendar intelligent importer | 3.0mm | UL746 | 130 | °C |
| RTIStr | 1.6mm | UL746 | 155 | °C |
| RTIStr | 3.0mm | UL746 | 155 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 177 | °C |
| Linear coefficient of thermal expansion | MD | | 5.3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | | IEC60243-1 | 37 | KV/mm |
| Leakage Trace Index | | IEC60112 | 125 | V |
| Surface resistivity | | IEC60093 | >1.0E+15 | ohms |
| Dielectric constant | 100Hz | IEC60250 | 3.10 | |
| Dielectric constant | 1MHz | IEC60250 | 3.10 | |
| Volume resistivity | | IEC60093 | >1.0E+13 | ohms·cm |
| Dissipation factor | 100Hz | IEC60250 | 8E-04 | |
| Dissipation factor | 1MHz | IEC60250 | 6.4E-03 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179 | NoBreak | |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | NoBreak | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 6.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 5.5 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180 | 6.0 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180 | 5.5 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | | ISO2039-1 | 135 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.