Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | -- | ASTMD792 | 1.18 | g/cm³ |
| Density/specific gravity | --2 | ASTMD792 | 1.22 | g/cm³ |
| Melt mass flow rate | 260°C/2.16kg | ASTMD1238 | 10 | g/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.60 | % |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.40to0.60 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.10 | % |
| Water absorption rate | 平衡,23°C | ASTMD570 | 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength 3 | 屈服 | ASTMD638 | 62.7 | Mpa |
| Elongation rate 4 | 断裂 | ASTMD638 | 40 | % |
| Bending modulus 4 | 100mmSpan | ASTMD790 | 2650 | Mpa |
| Flexural Strength4 | Yield,100mmSpan | ASTMD790 | 102 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 104 | °C |
| Hot deformation temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 90.6 | °C |
| Hot deformation temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 95.0 | °C |
| Vicat softening temperature | | ASTMD15255 | 113 | °C |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTMD696 | 7.2E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-30to30°C | ASTMD696 | 7.2E-05 | cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.20 | W/m/K |
| RTIElec | | UL746 | 85.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 85.0 | °C |
| RTIStr | | UL746 | 85.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | ASTMD257 | >1.0E+16 | ohms |
| Volume resistivity | | ASTMD257 | 1E+17 | ohms·cm |
| Dielectric strength | 3.20mm,inOil | ASTMD149 | 19 | KV/mm |
| Hot wire ignition | HWI | UL746 | PLC1 | |
| Dielectric constant | 50Hz | ASTMD150 | 3.00 | |
| Dielectric constant | 60Hz | ASTMD150 | 3.00 | |
| Dielectric constant | 100Hz | ASTMD150 | 3.00 | |
| Dissipation factor | 50Hz | ASTMD150 | 5E-03 | |
| Dissipation factor | 60Hz | ASTMD150 | 5E-03 | |
| Dissipation factor | 100Hz | ASTMD150 | 4.9E-03 | |
| Arc resistance 6 | | ASTMD495 | PLC6 | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC1 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC2 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 160 | J/m |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 530 | J/m |
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 54.2 | J |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 61.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R级 | ASTMD785 | 123 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| UL flame retardant rating | 2.5mm | UL94 | 5VB | |
| Extreme Oxygen Index | | ASTMD2863 | 32 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.