Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass Flow Rate (MFR) 260 ° C/2.16 kg | | ASTM D1238 | 10 | g/10min |
| Longitudinal shrinkage rate (Flow) | flow, 3.2 | Internal | 0.4~0.8 | |
| Longitudinal shrinkage rate (Flow) | xflow, 3.2 | Internal | 0.4~0.6 | |
| Water absorption rate | flow, 3.2 | ASTM D570 | 0.4 | |
| Water absorption rate | 24 hours | ASTM D570 | 0.1 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength yield (yld) | Type I, 50 | ASTM D638 | 62 | |
| Tensile elongation fracture (brk) | Type I, 50 | ASTM D638 | 40 | |
| Bending strength yield (yld) | 2.6 mm/ | ASTM D790 | 102 | |
| Bending modulus | 2.6 mm/ | ASTM D790 | 2650 | |
| combustion performance | Test Condition | Test Method | Test Result | Unit |
|---|
| UL fire rating V-0 | | UL94 | 1.5 | |
| UL fire rating 5VB | | UL94 | 2.49 | |
| Oxygen Index (LOI) | | ASTM D 2863 | 32 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Izod Notched -30 ℃ (-22 ℉) | | ASTM D256 | 160 | |
| Izod Notched at 23 ℃ (73 ℉) | | ASTM D256 | 534 | |
| Instrumented dart impact energy -30 ℃ (-22 ℉) peak | | ASTM D3763 | 54 | |
| Instrumented dart impact energy 23 ℃ (73 ℉) total energy | | ASTM D3763 | 61 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness R | | ASTM D785 | 123 | R |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | ASTM D257 | 100000000000000000 | ohm-cm |
| Surface resistivity | | ASTM D257 | 10000000000000000 | Ohm |
| Dielectric constant (DK) 50/60 Hz | | ASTM D 150 | 3 | |
| Dielectric constant (DK) 100Hz | | ASTM D 150 | 3 | |
| Dissipation factor (DF) 50/60 Hz | | ASTM D 150 | 50 | E-4 |
| Dissipation factor (DF) 100Hz | | ASTM D 150 | 49 | E-4 |
| Compared to the Leakage Traceability Index (CTI) | | UL 746A | 0 | plc |
| Insulation strength | in oil, 3.2 | ASTM D149 | 19.5 | |
| Arc resistance | | | 6 | plc |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746A | 2 | plc |
| Hot wire ignition (HWI) | | UL 746A | 1 | plc |
| High current arc ignition (HAI) | | UL 746A | 0 | plc |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | Rate B/50 | ASTM D1525 | 85 | °C |
| Relative Temperature Index (RTI) impact w/impact- | | UL 746B | 85 | °C |
| Relative Temperature Index (RTI) Electrical Elec- | | UL 746B | 85 | °C |
| Relative Temperature Index (RTI) intensity w/o impact- | | UL 746B | 85 | °C |
| Coefficient of Linear Expansion (CLTE) Longitudinal (Flow) | -30°C to 3 | ASTM E831 | 72 | E-6/°C |
| Coefficient of Linear Expansion (CLTE) Across Flow | -30°C to 3 | ASTM E831 | 72 | E-6/°C |
| thermal conductivity | | ASTM C 177 | 0.2 | W/m-°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.