Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD | 内部方法 | 0.40to0.70 | % |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 2.1 | g/10min |
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 21 | g/10min |
| Melt mass flow rate | 200°C/5.0kg | ISO1133 | 2.1 | g/10min |
| Melt mass flow rate | 220°C/10.0kg | ISO1133 | 21 | g/10min |
| density | | ASTMD792 | 1.04 | g/cm³ |
| density | 23°C | ISO1183 | 1.04 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | 屈服,23°C | ISO527-2 | 50.0 | Mpa |
| Bending stress | 23°C | ISO178 | 74.0 | Mpa |
| Tensile strength | 23°C | ASTMD638 | 50.0 | Mpa |
| Bending modulus | 23°C | ASTMD790 | 2450 | Mpa |
| Bending modulus | 23°C | ISO178 | 2450 | Mpa |
| bending strength | 23°C | ASTMD790 | 74.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,未退火,12.7mm | ASTMD648 | 84.0 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,12.7mm | ISO75-2/A | 84.0 | °C |
| Hot deformation temperature | 1.8MPa,退火 | ASTMD648 | 94.0 | °C |
| Hot deformation temperature | 1.8MPa,Annealed | ISO75-2/A | 94.0 | °C |
| Vicat softening temperature | | ASTMD15254 | 103 | °C |
| Vicat softening temperature | | ISO306/A | 103 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ISO180 | 290 | J/m |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 290 | J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.