Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | | ISO294-4 | 0.80 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 1.2 | % |
| Melt volume flow rate | 240°C/10.0kg | ISO1133 | 30.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending stress | | ISO178 | 62.0 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2 | 43.0 | Mpa |
| Tensile strain | 屈服,23°C | ISO527-2 | 3.5 | % |
| Tensile modulus | | ISO527-2 | 2000 | Mpa |
| Bending modulus | | ISO178 | 1800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | -- | ISO306/A50 | 160 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 102 | °C |
| Hot deformation temperature 2 | 0.45MPa,Annealed | ISO75-2/B | 85.0 | °C |
| Hot deformation temperature 2 | 1.8MPa,退火 | ISO75-2/A | 65.0 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Relative permittivity | 1MHz | IEC60250 | 2.90 | |
| Surface resistivity | | IEC60093 | 1E+14 | ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Dissipation factor | 1MHz | IEC60250 | 0.015 | |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Elongation MD | 断裂 | ISO527-3 | >50 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R级 | ISO2039-2 | 103 | |
| Ball pressure hardness | | ISO2039-1 | 86.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.