Technical Data Sheet
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation at break | 23℃ | % | ASTM D-638 | 2.3 |
| Tensile modulus | 23℃ | MPa | ASTM D-638 | 10700 |
| tensile strength | 23℃ | MPa | ASTM D-638 | |
| Bending modulus | 23℃ | MPa | ASTM D-790 | 8960 |
| bending strength | 23℃ | MPa | ASTM D-790 | 240 |
| Gap impact strength | -40℃ | J/m | ASTM D-256 | 85.0 |
| Gap impact strength | 23℃ | J/m | ASTM D-256 | 90.0 |
| Non notched impact strength | 23℃ | J/m | ASTM D-256 | 695 |
| Non notched impact strength | -40℃ | J/m | ASTM D-256 | |
| shear strength | 23℃ | MPa | ASTM D-732 | 74.5 |
| compressive strength | 23℃ | MPa | ASTM D-695 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 66psi，未退火 | ℃ | ASTM D-648 | 251 |
| Hot deformation temperature | 264psi，未退火 | ℃ | ASTM D-648 | 233 |
| Flame retardant grade | 1.5mm | | UL94 | HB |
| Flame retardant grade | 3.0mm | | UL94 | HB |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| density | 位移法 | g/cm | ASTM D-792 | 1.58 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.