Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃×5kgf(49N) | ASTM D-1238(ISO 1133) | 7.0 | g/10min |
| Shrinkage rate | 23℃ | ISO 622 | 0.3-0.5 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation | 23℃ | ASTM D-638(ISO 527) | 2.1 | |
| Tensile modulus | 23℃ | ASTM D-638(ISO 527) | 1.8(1770) | kg/cm2*104(MPa) |
| bending strength | 23℃ | ASTM D-790(ISO 178) | 800(78) | kg/cm2(MPa) |
| Tensile strength | 23℃ | ASTM D-638(ISO 527) | 420(41) | kg/cm2(MPa) |
| flexural modulus | 23℃ | ASTM D-790(ISO 178) | 3.4(3330) | kg/m2*104(MPa) |
| IZOD impact strength | 23℃，1/4” | ASTM D-256(ISO R180) | 1.8(18) | kg.cm/cm(J/m) |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | Annealed(80℃×2Hr1/8"厚) | ASTM D-648(ISO 75/A) | 88 | °C |
| vicat softening point | Annealed(80℃×2Hr1/8"厚) | ASTM D-1525(ISO 306B) | 93 | |
| Combustibility | FILE NOE162823,1/16" | UL 94 | HB | |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Residual monomer | | | 700 | ppm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.