Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.67 | |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.020 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 横向流量 | 内部方法 | 0.60 | % |
| Shrinkage rate | 流量 | 内部方法 | 0.20 | % |
| Water absorption rate | 饱和 | ASTM D570 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | | ASTM D638 | 157 | Mpa |
| elongation | 断裂 | ASTM D638 | 5.1 | % |
| Bending modulus | 23°C | ASTM D790 | 11800 | Mpa |
| Bending modulus | | ASTM D790/ISO 178 | 11800 | kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 158 | kg/cm²(MPa)[Lb/in²] |
| bending strength | 23°C | ASTM D790 | 158 | Mpa |
| Tensile elongation at break (elongation at break) | | ASTM D638/ISO 527 | 5.1 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | | ASTM D648/ISO 75 | 269 | ℃（℉） |
| Linear coefficient of thermal expansion | 流动 : 150°C | 内部方法 | 2.0E-6 | cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : 150°C | 内部方法 | 8.5E-5 | cm/cm/°C |
| Thermal deformation temperature under load | 1.8 MPa, 未退火 | ASTM D648 | 269 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation factor | 1 MHz | ASTM D150 | 0.026 | |
| Dissipation factor | 1.00 GHz | ASTM D150 | 4.0E-3 | |
| Leakage Trace Index | | IEC 60112 | 175 | V |
| Dielectric constant | 1 MHz | ASTM D150 | 3.80 | |
| Dielectric constant | 1.00 GHz | ASTM D150 | 3.50 | |
| Arc resistance | | ASTM D495 | 124 | sec |
| Volume resistivity | | ASTM D257 | 1.0E+15 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 130 | °C |
| Processing (melt) temperature | | | 350 | °C |
| Mold temperature | | | 40 到 160 | °C |
| Maintain pressure | | | 20.0 到 40.0 | Mpa |
| drying time | | | 4.0 到 24 | hr |
| Temperature at the rear of the barrel | | | 280 到 320 | °C |
| Temperature in the middle of the barrel | | | 320 到 340 | °C |
| Temperature at the front of the material cylinder | | | 340 到 360 | °C |
| Spray nozzle temperature | | | 340 到 360 | °C |
| Back pressure | | | 1.00 到 5.00 | Mpa |
| Screw speed | | | 50 到 100 | rpm |
| Injection pressure | | | 80.0 到 160 | Mpa |
| Injection speed | | | 中等偏快 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Non notched cantilever beam impact | 6.40 mm | ASTM D256 | 250 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R 级 | ASTM D785 | 106 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Extreme Oxygen Index | | ISO 527-1,-2(JIS K7161,7162) | 40 | % |
| UL flame retardant rating | 0.30 mm, ALL | UL 94 | V-0 | |
| Soldering Resistance | | 内部方法 | 300 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.