PPO NORYL™ GFN2 SABIC INNOVATIVE US
373
- Properties:enhanceGlass fiber reinforcedGlass fiber reinforced
- Usages:packingHousehold appliancesHousehold appliancesAutomotive interior parts
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20to0.50 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.060 | % |
| Melt mass flow rate | 300°C/5.0kg | ASTMD1238 | 9.0 | g/10min |
| Melt volume flow rate | 300°C/5.0kg | ISO1133 | 8.10 | cm3/10min |
| Outdoor applicability | UL746C | f1 | ||
| Density/specific gravity | ASTMD792 | 1.20 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strength 5,6 | ISO178 | 167 | Mpa | |
| Bending modulus 5 | ISO178 | 6540 | Mpa | |
| Elongation rate 4 | 断裂 | ASTMD638 | 2.6 | % |
| Tensile modulus 2 | ASTMD638 | 6200 | Mpa | |
| Tensile strength 3 | 断裂 | ASTMD638 | 90.0 | Mpa |
| Bending modulus 4 | 50.0mm跨距 | ASTMD790 | 5800 | Mpa |
| Bending strength 4 | 屈服,50.0mm跨距 | ASTMD790 | 160 | Mpa |
| Tensile stress | 断裂 | ISO527-2/5 | 97.3 | Mpa |
| Tensile strain | 断裂 | ISO527-2/5 | 2.5 | % |
| Tensile modulus | ISO527-2/1 | 7070 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 135 | °C |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 138 | °C | |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 141 | °C | |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 143 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 143 | °C |
| -- | ISO306/B120 | 146 | °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 2.9E-05 | cm/cm/°C |
| TD：-40到40°C | ASTME831 | 8.3E-05 | cm/cm/°C | |
| RTIElec | UL746 | 90.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 90.0 | °C | |
| RTIStr | UL746 | 90.0 | °C | |
| Hot deformation temperature 8 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 137 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 143 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance 9 | ASTMD495 | PLC7 | ||
| High arc combustion index | HAI | UL746 | PLC4 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC4 | |
| Hot wire ignition | HWI | UL746 | PLC4 | |
| Dissipation factor | 50Hz | ASTMD150 | 8E-04 | |
| 60Hz | ASTMD150 | 8E-04 | ||
| Dielectric strength | 3.20mm,inOil | ASTMD149 | 17 | KV/mm |
| Dielectric constant | 50Hz | ASTMD150 | 2.86 | |
| 60Hz | ASTMD150 | 2.86 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 22.6 | J |
| NotchedIzodImpactStrength7 | 23°C | ISO180/1A | 11 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/2C | 12 | kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ASTMD256 | 96 | J/m |
| 23°C | ASTMD256 | 120 | J/m | |
| 23°C | ASTMD4812 | 650 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | L计秤 | ASTMD785 | 106 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ASTMD2863 | 26 | % | |
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.