Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | | | | % |
| Rockwell hardness | | ASTM D-758(M级) | 97 | |
| Light transmittance | | ASTM D-1003 | 92 | % |
| Refractive index N | | ASTM D-542 | 1.49 | |
| Density/specific gravity | | ASTM D-792 | 1.19 | |
| Forming shrinkage rate | (冷模/冷件),48hrs | ASTM D-935 | 0.2-0.6 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| impact strength | Izod 研磨缺口 | ASTM D256 | 1.2(12.3) | kgf-cm/cm(J/m) |
| impact strength | 落锤(15.2×15.2×0.3cm重1.4kg半径0.64cm) | ASTM D256 | 14(1.4) | kg-cm(J) |
| flexural modulus | | ASTM D-790 | 32000 | Kgf/cm |
| tensile strength | 初级应变速度0.1cm/cm/min | ASTM D-638 | 720(70) | Kgf/cm |
| bending strength | 横跨比=16 | ASTM D-790 | 1050(103) | Kgf/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| vicat softening point | 50℃/hr,1kg | ASTM D-1525，未退火 | 111 | °C |
| vicat softening point | 50℃/hr,5kg | ASTM D-1525，未退火 | 104 | °C |
| Glass transition temperature | Tg | | 108 | °C |
| Temperature range for use | 与残余应力大小有关 | | 85-102 | °C |
| Heat deformation temperature load, annealing | 2℃/min,18.6kgf/cm | ASTM D-648 | 102 | °C |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 浸水24hrs后增重 | ASTM D-570 | 0.3 | % |
| Melt index | | ASTM D-1238 | 3.5 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.