Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.18 | |
| Molding shrinkage rate | | ASTM D955 | 0.7 | % |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 26 | g/10min |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation at break | | ASTM D638/ISO 527 | >50 | % |
| Tensile modulus | | ASTM D638/ISO 527 | 2700 | kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D638/ISO 527 | 45 | kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 4 | % |
| Tensile elongation at break (elongation at break) | | ASTM D638/ISO 527 | >50 | % |
| IZOD notch impact strength | | ASTM D256/ISO 179 | N | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | | ASTM D648/ISO 75 | 80 | ℃（℉） |
| Hot deformation temperature | | ASTM D648/ISO 75 | 90 | ℃（℉） |
| melting point | | | 240 | ℃（℉） |
| vicat softening point | | ASTM D1525/ISO R306 | 93 | ℃（℉） |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 0.76 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | ASTM D257/IEC 60093 | 1E16 | Ω |
| Dielectric constant | | ASTM D150/IEC 60250 | 3.2 | |
| Dielectric constant | | ASTM D150/IEC 60250 | 3.1 | |
| Arc resistance | | ASTM D495/IEC 60112 | 350 | |
| Volume resistivity | | ASTM D257/IEC 60093 | 1E14 | Ω.cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.