Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Mold shrinkage rate | 3.2mm(0.125in) | ASTM D-955 | 0.002-0.006 | in/in |
| Haze | | ASTM D-1003 | 0.3 | % |
| Total transmittance | | ASTM D-1003 | 91 | % |
| Density/specific gravity | | ASTM D-792 | 1.19 | g/cm |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural yield strength | | ASTM D-790 | 10000 | psi |
| Tensile yield stress/fracture stress | | ASTM D-638 | 7100/7500 | psi |
| Yield elongation/fracture elongation | | ASTM D-638 | 5/300 | % |
| Flexural modulus | | ASTM D-790 | 2.9×105 | psi |
| IZOD notch impact strength | 23℃/-40℃ | ASTM D-256 | 1.5/0.8 | ft-lb/in |
| Rockwell hardness | | ASTM D-785 | 107 | R |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa(66PSi) | ASTM D-648 | 70/65 | °C |
| Hot deformation temperature | 1.82MPa(264PSi) | ASTM D-648 | 65 | °C |
| Vicat softening temperature | 1kg负荷 | ASTM D-1525 | 85 | °C |
| Combustibility | 1.5mm | UL 94 | V-2 | |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Intrinsic viscosity | | | 0.62 | |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 230℃,5kg | | 22.5 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.