Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | ISO294-4 | 1.3 | % |
| Shrinkage rate | MD | ISO294-4 | 0.90 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.70 | % |
| Melt mass flow rate | 235°C/2.16kg | ISO1133 | 13 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending stress | | ISO178 | 60.0 | Mpa |
| Tensile stress | 屈服 | ISO527-2 | 46.0 | Mpa |
| Tensile strain | 屈服 | ISO527-2 | 4.0 | % |
| Tensile strain | 断裂 | ISO527-2 | 200 | % |
| Bending modulus | | ISO178 | 1600 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 85.0 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 45.0 | °C |
| Melting temperature (DSC) | | ISO3146 | 178 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.3E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | IEC60093 | 1E+15 | ohms·cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R计秤 | ISO2039-2 | 105 | |
| Shore hardness | 邵氏D | ISO868 | 78 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.