Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：3.20mm | | 0.20 | % |
| Shrinkage rate | TD：3.20mm | | 0.50 | % |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.020 | % |
| Density/specific gravity | | ASTMD792 | 1.69 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | | ASTMD638 | 179 | Mpa |
| Tensile stress | | ISO527-2 | 180 | Mpa |
| elongation | 断裂 | ASTMD638 | 1.5 | % |
| Tensile strain | 断裂 | ISO527-2 | 1.4 | % |
| Bending modulus | | ASTMD790 | 14500 | Mpa |
| Bending modulus | | ISO178 | 14000 | Mpa |
| bending strength | | ASTMD790 | 255 | Mpa |
| Bending stress | | ISO178 | 260 | Mpa |
| compressive strength | | ASTMD695 | 285 | Mpa |
| Poisson's ratio | | | 0.39 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD：-50到50°C | ASTME831 | 2E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | MD：100到200°C | ASTME831 | 1.5E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-50到50°C | ASTME831 | 4E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：100到200°C | ASTME831 | 9E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：导热系数 | ASTME831 | 0.30 | W/m/K |
| UL temperature rating | | UL746B | 200to220 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 265 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation factor | 25°C,1kHz | ASTMD150 | 2E-03 | |
| Dissipation factor | 25°C,1MHz | ASTMD150 | 3E-03 | |
| Arc resistance | | ASTMD495 | 125 | sec |
| Compared to the anti leakage trace index | CTI | UL746 | 130 | V |
| InsulationResistance2 | 90°C | | 1E+11 | ohms |
| Volume resistivity | | ASTMD257 | 1E+16 | ohms·cm |
| Dielectric strength | | ASTMD149 | 22 | KV/mm |
| Dielectric constant | 25°C,1kHz | ASTMD150 | 3.80 | |
| Dielectric constant | 25°C,1MHz | ASTMD150 | 3.90 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 3.17mm | ASTMD256 | 80 | J/m |
| Impact strength of cantilever beam gap | | ISO180/A | 8.0 | kJ/m² |
| Cantilever beam without notch impact strength | 3.18mm | ASTMD4812 | 510 | J/m |
| Unscented Izod impact strength | | ISO180 | 30 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M计秤 | ASTMD785 | 102 | |
| Rockwell hardness | R计秤 | ASTMD785 | 120 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FlameRating | 1.6mm | UL94 | V-05VA | |
| Extreme Oxygen Index | | ASTMD2863 | 53 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.