Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.57 | |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.01 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 23°C,24hr | ISO62 | 0.030 | % |
| Shrinkage rate | 流动方向，80℃×2mmt | | 0.3 | % |
| Shrinkage rate | 垂直方向，80℃×2mmt | | 0.6 | % |
| Melt viscosity | 310°C,1000sec^-1 | ISO11443 | 350000 | mPa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported notched beam | | ISO 179/1eA | 10.0 | kJ/m² |
| Fracture strain | | ISO 527-1,2 | 2 | % |
| Bending stress | | ISO178 | 245 | Mpa |
| Tensile stress | | ISO527-2 | 170 | Mpa |
| Tensile strain | 断裂 | ISO527-2 | 2.0 | % |
| tensile strength | | ASTM D638/ISO 527 | 170 | kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ISO 527-1,2 | 170 | Mpa |
| Bending modulus | | ASTM D790/ISO 178 | 10000 | kg/cm²(MPa)[Lb/in²] |
| Bending modulus | | ISO178 | 10000 | Mpa |
| Bending modulus | | ISO 178 | 10000 | Mpa |
| bending strength | | ISO 178 | 245 | Mpa |
| bending strength | | ASTM D790/ISO 178 | 245 | kg/cm²(MPa)[Lb/in²] |
| Tensile elongation at break (elongation at break) | | ASTM D638/ISO 527 | 2 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Combustibility (rate) | | UL94 | V-0 | |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 260 | °C |
| Linear coefficient of thermal expansion | 流动方向 | ISO 11359-2 | 2 | ×10-5/℃ |
| Linear coefficient of thermal expansion | 垂直方向 | | 4 | ×10-5/℃ |
| Linear coefficient of thermal expansion | MD | 内部方法 | 2E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | 内部方法 | 4E-05 | cm/cm/°C |
| Load deformation temperature | 1.8MPa | ISO 75-1 | 260 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric loss factor | 3mmt | IEC 60243-1 | 16 | KV/mm |
| Dielectric strength | 3.00mm | IEC60243-1 | 16 | KV/mm |
| Relative permittivity | 1kHz | IEC60250 | 4.00 | |
| Relative permittivity | 1MHz | IEC60250 | 4.00 | |
| Leakage Trace Index | | IEC60112 | 150 | V |
| Resistant to conductive tracks | | IEC 60112 | 150 | V |
| Surface resistivity | | IEC 60093 | 2×1017 | Ω |
| Volume resistivity | | IEC 60093 | 3×1016 | Ω·cm |
| Volume resistivity | | ASTM D257/IEC 60093 | 3.0 x 10^16 | Ω.cm |
| Volume resistivity | | IEC60093 | 3E+16 | ohms·cm |
| Dissipation factor | 1kHz | IEC60250 | 1E-03 | |
| Dissipation factor | 1MHz | IEC60250 | 2E-03 | |
| Dissipation factor | 耐电弧性 | IEC60250 | 124 | sec |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M级 | ISO2039-2 | 105 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | V-0 | |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt viscosity | 310℃,1000/sec | ISO 11443 | 350 | Pa·s |
| Water absorption rate | 23℃,水中24小时 | ISO 62 | 0.01 | % |
| density | | ISO 1183 | 1.57 | g/cm³ |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| ColourNumber | | | HF2000/HD9050 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.