Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Mold shrinkage rate | 料流方向 | ASTM D955 | 0.4-0.7 | % |
| Melt mass flow rate | 240℃，5kg | ASTM D1238 | 25 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | 50mm/min | ASTM D638 | 640 | kg/cm2 |
| Elongation at break | 50mm/min | ASTM D638 | 120 | % |
| Bending strength | 15mm/min | ASTM D790 | 1100 | kg/cm2 |
| Bending modulus | 15mm/min | ASTM D790 | 28000 | kg/cm2 |
| Rockwell hardness | 23℃ | ASTM D785 | 120 | R scale |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.82MPa，1/4”，不退火 | ASTM D648 | 89 | °C |
| Vicat softening point | 50N，50℃/h，不退火 | ASTM D1525 | 99 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 1/8”，23℃ | ASTM D256 | 600 | J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.