Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 372°C/5.0kg | ASTMD1238 | 10到17 | g/10min |
| Apparent density | | JISK6891 | 1.00到1.40 | g/cm³ |
| Water absorption rate | 饱和 | ASTMD570 | <0.010 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation | 断裂 | JISK6891 | 350到450 | % |
| Bending modulus | | ASTMD790 | 580到690 | Mpa |
| Tensile strength | 屈服 | JISK6891 | 25.4到30.4 | Mpa |
| compressive strength | 1%应变 | ASTMD695 | 4.90到5.90 | Mpa |
| compressive strength | 25%应变 | ASTMD695 | 31.4到33.3 | Mpa |
| compressive strength | 摩擦系数(与钢-静态) | ASTMD695 | 0.040到0.050 | |
| Compressive modulus | | ASTMD695 | 490到590 | Mpa |
| Flexural Strength | | ASTMD790 | Nobreak | |
| Load deformation | 25°C,14MPa3 | ASTMD621 | 8.00到9.00 | % |
| Load deformation | 100°C,6.9MPa2 | ASTMD621 | 2.00到3.00 | % |
| Load deformation | 100°C,6.9MPa3 | ASTMD621 | 8.50到9.50 | % |
| Load deformation | 25°C,14MPa2 | ASTMD621 | 2.50到3.00 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| specific heat | | | 1050 | J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.26 | W/m/K |
| Linear coefficient of thermal expansion | MD：20到100°C | ASTMD696 | 1.2E-04 | cm/cm/°C |
| Melting temperature | | ASTMD4591 | 300到310 | °C |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt viscosity | 380°C | | 2.00E+6到2.50E+7 | mPa·s |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | 邵氏D | ASTMD2240 | 60到70 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | V-0 | |
| Extreme Oxygen Index | 1.57mm | ASTMD2863 | >95 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.