ABS/PC CYCOLOY™ CX7240-7M1D218 SABIC INNOVATIVE NANSHA

612

Properties:
Flame retardant
High impact resistance
High mobility
Usages:
Electrical field
Electronic field
Electronic display
Engine hood parts
Aerospace Applications
Nursing supplies
Construction field
Outdoor applications
Liquid handling
Medical supplies
Lighting fixtures
Compare
View Prices

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Melt flow rate	260°C/2.16 kg	ASTM D1238	18	g/10 min
Molten Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	15.0	cm3/10min
Shrinkage rate - flow	3.20 mm	内部方法	0.40 到 0.60	%
Water absorption rate	饱和, 23°C	ISO 62	0.20	%
Water absorption rate	Water absorption rate	平衡, 23°C, 50% RH	ISO 62	0.10	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	-- 2	ASTM D638	2600	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2600	Mpa
Tensile strength	屈服 3	ASTM D638	65.0	Mpa
	Tensile strength	屈服	ISO 527-2/50	65.0	Mpa
		Tensile strength	断裂 3	ASTM D638	58.0	Mpa
		Tensile strength	Tensile strength	断裂	ISO 527-2/50	50.0	Mpa
elongation	屈服 3	ASTM D638	4.1	%
	elongation	屈服	ISO 527-2/50	4.0	%
		elongation	断裂 3	ASTM D638	100	%
		elongation	elongation	断裂	ISO 527-2/50	90	%
Bending modulus	50.0 mm 跨距 4	ASTM D790	2500	Mpa
Bending modulus	Bending modulus	-- 5	ISO 178	2500	Mpa
Bending stress	-- 5, 6	ISO 178	96.0	Mpa
Bending stress	Bending stress	屈服, 50.0 mm 跨距 4	ASTM D790	104	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Thermal deformation temperature under load	0.45 MPa, 未退火, 3.20 mm	ASTM D648	100	°C
	Thermal deformation temperature under load	1.8 MPa, 未退火, 3.20 mm	ASTM D648	89.0	°C
		Thermal deformation temperature under load	1.8 MPa, 未退火, 6.40 mm	ASTM D648	99.0	°C
		Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10	ISO 75-2/Af	93.0	°C
Vicat softening temperature	--	ASTM D152511, ISO 306/B5011	110	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	113	°C
Ball Pressure Test	73 到 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	流动 : -40 到 40°C	ASTM E831, ISO 11359-2	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	横向 : -40 到 40°C	ASTM E831	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : -40°C	ISO 11359-2	7.5E-5	cm/cm/°C
thermal conductivity		ISO 8302	0.20	W/m/K
RTI Elec		UL 746	90.0	°C
RTI Imp		UL 746	90.0	°C
RTI		UL 746	90.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm
Dielectric strength	0.800 mm, 在油中	IEC 60243-1	35	KV/mm
	Dielectric strength	1.60 mm, 在油中	IEC 60243-1	25	KV/mm
	Dielectric strength	Dielectric strength	3.20 mm, 在油中	IEC 60243-1	17	KV/mm
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 3
High arc combustion index (HAI) 12		UL 746	PLC 0
Hot wire ignition (HWI)		UL 746	PLC 3

injection	Test Result	Unit
drying temperature	80 到 90	°C
drying time	2.0 到 4.0	hr
Suggested maximum moisture content	0.020	%
Hopper temperature	60 到 80	°C
Temperature at the rear of the barrel	230 到 280	°C
Temperature in the middle of the barrel	240 到 290	°C
Temperature at the front of the material cylinder	250 到 300	°C
Spray nozzle temperature	250 到 300	°C
Processing (melt) temperature	250 到 300	°C
Mold temperature	60 到 85	°C
Exhaust hole depth	0.030 到 0.075	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	65.0	J

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.60 mm	UL 94	V-1
	UL flame retardant rating	0.75 mm	UL 94	V-0
		UL flame retardant rating	1.5 mm	UL 94	5VB
		UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	0.75 mm	IEC 60695-2-12	960	°C
Burning wire flammability index	Burning wire flammability index	0.75 mm 13	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.75 mm 13	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	825	°C
		Hot filament ignition temperature	1.5 mm 13	IEC 60695-2-13	775	°C
			Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	800	°C
			Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm 13	IEC 60695-2-13	775	°C
Extreme Oxygen Index		ISO 4589-2	34	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.