Technical Data Sheet
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Cantilever beam without notch impact strength | | D256 | 34.1 | J/m |
| Physical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | D792 | 0.94 | g/cm³ |
| Water absorption rate | | D570 | < 0.01 | % |
| Melt mass flow rate | 260 ℃，1.2 Kg | D1238 | 5.5 | g/10 min |
| Melt mass flow rate | 280 ℃，1.2 Kg | D1238 | 21 | g/10 min |
| Melt mass flow rate | 300 ℃，1.2 Kg | D1238 | 62.5 | g/10 min |
| Melting point | | 内部方法 | 129 | °C |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | 屈服 | D638 | 33.5 | Mpa |
| Tensile strength | 断裂 | D638 | 33.6 | Mpa |
| Tensile strength | 拉伸模量 | D638 | 2600 | Mpa |
| Bending strength | | D790 | 74.2 | Mpa |
| Bending modulus | | D790 | 2600 | Mpa |
| Tensile strain | 断裂 | D638 | 7.6 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | D1525 | 128 | °C |
| Hot deformation temperature | 0.45 MPa | D648 | 115 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices