Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | (23°C,24hr) | ISO62 | 0.01 | % |
| Melt flow index | 190℃/2.16Kg | ISO1133 | 1.8 | g/10min |
| Melt flow index | 230℃/2.16Kg | ISO1133 | 11 | g/10min |
| Melt flow index | 水蒸气渗透性 | | 3.70 | gmil/(m2day |
| Melt flow index | 氧渗透 | | 997 | cm3mil/(m2dayatm |
| Melt flow index | 水蒸气穿透率 | ISO15106-3 | 0.0008 | g/m²/day |
| Melt flow index | 厚度 | | 70 | microns |
| Melt flow index | 260℃/2.16Kg | ISO1133 | 32 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| tensile strength | 23°C | ISO527-2 | 63 | Mpa |
| elongation at break | 23°C | ISO527-2 | 4.5 | % |
| Tensile modulus | 23°C | ISO527-2 | 2600 | Mpa |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 2.6 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 20 | kJ/m² |
| elongation at break | MD,23°C | ISO527-2 | 2.9 | % |
| elongation at break | TD,23°C | ISO527-2 | 3 | % |
| Tensile modulus | TD,23°C | ISO527-2 | 1800 | Mpa |
| Tensile modulus | MD,23°C | ISO527-2 | 2200 | Mpa |
| Tensile modulus | 断裂拉伸强度 | ISO527-3 | 57 | Mpa |
| Tensile modulus | 断裂拉伸强度 | ISO527-3 | 50 | Mpa |
| Tensile modulus | Elmendorf撕裂强度 | ISO6383-2 | 225 | g |
| Tensile modulus | Elmendorf撕裂强度 | ISO6383-2 | 230 | g |
| Tensile modulus | 跌落试验 | ISO7765-1 | <=36 | g |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa未退火 | ISO75-2/Bf | 75 | °C |
| Vicat softening temperature | | ISO306/B50 | 80 | °C |
| Vicat softening temperature | 玻璃转化温度 | ISO11357-2 | 78 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistance | | IEC60093 | 1E+14 | Ω.cm |
| Dielectric constant | 23°C | IEC60250 | 2.35 | 1kHz |
| Dissipation factor | 相对漏电起痕指数 | IEC60112 | 600 | V |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ISO489 | 1.53 | °C |
| Transmittance 2000 μ m | | ISO13468-2 | 91 | % |
| Haze μ m | | ISO13468-2 | <=0.1 | % |
| gloss | | ISO2813 | >=100 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.