Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD | ASTM D955 | < 0.40 | % |
| Shrinkage rate | MD | ASTMD955 | <0.40 | % |
| Water absorption rate | 饱和 | ASTMD570 | <0.30 | % |
| Water absorption rate | 饱和 | ASTM D570 | < 0.30 | % |
| Melt flow rate | 200℃/5.0 kg | ASTM D1238 | 0.6 | g/10 min |
| Melt flow rate | 220℃/10.0 kg | ASTM D1238 | 6 | g/10 min |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 0.60 | g/10min |
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 6.0 | g/10min |
| Density/specific gravity | | ASTMD792 | 1.03 | g/cm³ |
| Density/specific gravity | | ASTM D792 | 1.03 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending strength 4 | 屈服,23°C | ASTMD790 | 58.6 | Mpa |
| Bending modulus 3 | 23°C | ASTMD790 | 2070 | Mpa |
| Tensile strength 2 | 屈服,23°C,3.18mm | ASTMD638 | 38.6 | Mpa |
| Elongation rate 2 | 断裂,23°C,3.18mm | ASTMD638 | 40 | % |
| Tensile strength 2 | Break,23°C,3.18mm | ASTMD638 | 31.7 | Mpa |
| elongation | 断裂, 23℃, 3.18 mm | ASTM D638 | 40 | % |
| Rockwell hardness | R 级, 23℃ | ASTM D785 | 100 | |
| Bending modulus | 23℃ | ASTM D790 | 2070 | Mpa |
| bending strength | 屈服, 23℃ | ASTM D790 | 58.6 | Mpa |
| Tensile strength | 屈服, 23℃, 3.18 mm | ASTM D638 | 38.6 | Mpa |
| Tensile strength | 断裂, 23℃, 3.18 mm | ASTM D638 | 31.7 | Mpa |
| Impact strength of cantilever beam gap | 23℃, 3.18 mm | ASTM D256 | 360 | J/m |
| Impact strength of cantilever beam gap | 23℃, 6.35 mm | ASTM D256 | 310 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTM D1525 | 101 | °C |
| Hot deformation temperature | 1.8 MPa, 退火, 12.7 mm | ASTM D648 | 85 | °C |
| Hot deformation temperature | 1.8MPa,未退火,12.7mm | ASTMD648 | 85.0 | °C |
| Vicat softening temperature 4 | | ASTMD15255 | 101 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTMD256 | 360 | J/m |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 310 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R计秤,23°C | ASTMD785 | 100 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare