Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | % | 0.80到1.0 | -- |
| Shrinkage rate | MD | % | 0.80到1.0 | -- |
| Melt mass flow rate | 240°C/5.0kg | g/10min | 14 | -- |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | | MPa | 45.0 | 40.0 |
| Tensile strain | 断裂 | % | >80 | |
| Bending stress | | MPa | 60.0 | 50.0 |
| Bending modulus | 23°C | MPa | 1800 | 1600 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | -- | °C | 190 | -- |
| Vicat softening temperature | -- | °C | 110 | -- |
| Hot deformation temperature 1 | 0.45MPa,未退火 | °C | 96.0 | -- |
| Hot deformation temperature 1 | 1.8MPa,未退火 | °C | 62.0 | -- |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | 邵氏D,15秒 | | 62 | -- |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | | HB | -- |
| Hot filament ignition temperature | 2.0mm | °C | 650 | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.