Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ISO1183 | 1.42 | g/cm³ |
| Melt mass flow rate | | ISO1133 | 25 | g/10min |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 21.0 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.9 | % |
| Shrinkage rate | MD | ISO294-4 | 1.9 | % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 1.4 | % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2 | 3300 | Mpa |
| Tensile stress | 屈服 | ISO527-2 | 71.0 | Mpa |
| Tensile strain | 屈服 | ISO527-2 | 12 | % |
| Nominal tensile fracture strain | | ISO527-2 | 23 | % |
| TensileCreepModule | 1hr | ISO899-1 | 2800 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 1500 | Mpa |
| Bending modulus | | ISO178 | 3000 | Mpa |
| CoefficientFriction | vs.Itself-Dynamic,1hr | ASTMD1894 | 0.25 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| AnnealingTemperature | | | 160 | °C |
| AnnealingTime-Optional | | | 30.0 | min/mm |
| EffectiveThermalDiffusivity | | | 8E-08 | m²/s |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 162 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 94.0 | °C |
| Vicat softening temperature | | ISO306/B50 | 160 | °C |
| Melting temperature 2 | | ISO11357-3 | 178 | °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ASTME831 | 1E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | >1.0E+15 | ohms |
| Volume resistivity | | IEC60093 | 1E+14 | ohms·cm |
| Relative permittivity | 100Hz | IEC60250 | 3.80 | |
| Relative permittivity | 1MHz | IEC60250 | 3.80 | |
| Leakage Trace Index | | IEC60112 | 600 | V |
| Hot-wireIgnition | 0.750mm | UL746 | 8.0 | sec |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 8.0 | kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 200 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 200 | kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 8.0 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 7.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M计秤 | ISO2039-2 | 92 | |
| Rockwell hardness | R计秤 | ISO2039-2 | 120 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning rate 3 | 1.00mm | ISO3795 | 20 | mm/min |
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 0.8mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| Extreme Oxygen Index | | ISO4589-2 | 23 | % |
| FMVSS flammability | | FMVSS302 | B | |
| atomization | F-value(refraction) | ISO6452 | 95 | % |
| atomization | G-value(condensate) | ISO6452 | 2E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| Emission | | VDA275 | <8.00 | mg/kg |
| EmissionofOrganicCompounds | | VDA277 | 4.30 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.