Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD | ASTMD955 | 0.50到0.70 | % |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.15 | % |
| Water absorption rate | 平衡,23°C,50%RH | ASTMD570 | 0.32 | % |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
| Density/specific gravity | | ASTMD792 | 1.20 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Wear resistance - AngelinHaze2 | | ASTMD1004 | 45 | % |
| Tensile strength | 屈服,23°C1 | ASTMD638 | 60.0 | Mpa |
| Tensile strength | 断裂 | ASTMD638 | 71.0 | Mpa |
| Tensile modulus | | ASTMD638 | 2410 | Mpa |
| elongation | 屈服 | ASTMD638 | 6.0 | % |
| elongation | 断裂 | ASTMD638 | 150 | % |
| Bending modulus | | ASTMD790 | 2410 | Mpa |
| bending strength | | ASTMD790 | 96.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,退火,4.00mm | ASTMD648 | 144 | °C |
| Hot deformation temperature | 1.8MPa,未退火,4.00mm | ASTMD648 | 128 | °C |
| Hot deformation temperature | 1.8MPa,退火,4.00mm | ASTMD648 | 141 | °C |
| Vicat softening temperature | | ASTMD15255 | 149 | °C |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTMD696 | 6.8E-05 | cm/cm/°C |
| Ball pressure temperature | | IEC60598-1 | >125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Leakage Trace Index | 2.00mm | IEC60112 | 250 | V |
| Dielectric strength | | ASTMD149 | 17 | KV/mm |
| Dissipation factor | 60Hz | ASTMD150 | 1E-03 | |
| Dielectric constant | 60Hz | ASTMD150 | 3.00 | |
| Volume resistivity | 23°C | ASTMD257 | 2E+17 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Cantilever beam without notch impact strength | 23°C | ASTMD256 | 无断裂 | |
| Dart impact equipped with measuring instruments 4 | 23°C,3.20mm,TotalEnergy | ASTMD3763 | 87.0 | J |
| Suspended wall beam gap impact strength 3 | 23°C,3.20mm | ASTMD256 | 900 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M级 | ASTMD785 | 73 | |
| Rockwell hardness | R级 | ASTMD785 | 118 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ASTMD542 | 1.586 | |
| Haze | | ASTMD1003 | 0.70到1.5 | % |
| transmissivity | | ASTMD1003 | 89.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot filament ignition temperature 6 | 2.00mm | IEC60695-2-13 | 850 | °C |
| UL flame retardant rating | 3.00mm | UL94 | HB | |
| UL flame retardant rating | 0.500mm | UL94 | V-2 | |
| UL flame retardant rating | 1.60mm | UL94 | V-2 | |
| UL flame retardant rating | 2.50mm | UL94 | V-2 | |
| UL flame retardant rating | 2.70mm | UL94 | V-2 | |
| Extreme Oxygen Index | | ASTMD2863 | 26 | % |
| Average degree of combustion | | ASTMD635 | 3 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.