Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Light transmittance | 3mm厚 | ASTM D-1003 | 85-89 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural elasticity | | ISO 178 (ASTM D-790) | 2350 | Mpa |
| Taber wear amount | 1,000round | ASTM D-1044 | 12 | mg |
| Intensity of tension and subsidence | | ISO R-527 (ASTM D-638) | 64 | Mpa |
| Flexural strength | | ISO 178 (ASTM D-790) | 93 | Mpa |
| Tensile elasticity | | ISO R-527 (ASTM D-638) | 2300 | Mpa |
| Rockwell hardness | | ISO 2039-2 (ASTM D-785) | 120 | R |
| Tensile strength | | ISO R-527 (ASTM D-638) | 68 | Mpa |
| Tensile failure rate | | ISO R-527 (ASTM D-638) | 115 | % |
| IZOD impact strength | 4mm with notch 3.2mm with notch | ISO 180 (ASTM D-256) | 70 | KJ/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| vicat softening point | | ISO 306 | 148 | °C |
| Combustibility | 1.47mm厚 | UL-94 | V-2 | |
| Coefficient of linear expansion | | ASTM D-696 (ASTM D-695) | 6.5 | |
| Hot deformation temperature | 1.8Mpa 18.6kg/cm | ISO 75 (ASTM D-648) | 132 | °C |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Forming shrinkage rate | | ASTM D-955 | 0.5-0.7 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 300℃ 1.2kg | ISO 1133 (ASTM D-1238) | 12 | g/10min |
| Density/specific gravity | | ASTM D-792 | 1.2 | g/cm |
| Water absorption rate | 23℃水中24h | ASTM D-570 | 0.23 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.