Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | | ASTM D955 | ≤0.5 | % |
| Rockwell hardness | 23℃ | ASTM D785 | 83 | |
| Liquidity index | 200℃;5kg荷重 | ASTM D1238 | 2.5 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength - surrender point | 23℃,1/8英寸,5mm/min | ASTM D638 | 710 | kg/cm2 |
| Tensile strength - fracture point | 23℃,1/8英寸,5mm/min | ASTM D638 | 700 | kg/cm2 |
| IZOD Impact Strength | 23℃,1/4英寸,切割 | ASTM D256 | 1.8 | kg-cm/cm |
| IZOD Impact Strength | 23℃,1/8英寸,切割 | ASTM D256 | 1.9 | kg-cm/cm |
| Flexural coefficient | 23℃,2.8mm/min | ASTM D790 | 34000 | kg/cm2 |
| Flexural strength | 23℃,2.8mm/min | ASTM D790 | 1100 | kg/cm2 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame retardancy | 1/16英寸 | UL94 | HB | |
| Hot deformation temperature | 未退火,1/2英寸,18.56kg/cm²荷重压力 | ASTM D648 | 91 | °C |
| Vicat softening temperature | 1/8英寸,1kg荷重 | ASTM D1525 | 104 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.