Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D1505 | 0.941 | g/cm² |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 8.0 | g/10min |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 8.0 | g/10min |
| Vinyl acetate content | | | 18.0 | wt% |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| tensile strength | | ASTM D-1708 | 18 | Mpa |
| elongation | 断裂 | ASTM D-1708 | 600-900 | % |
| Tensile modulus | | ASTM D-1708 | 51 | Mpa |
| Shore hardness | | ASTM D-2240 | 90 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| melting point | DSC | ASTM D-3418 | 86 | °C |
| vicat softening point | | ASTM D-1525 | 61 | °C |
| softening point | | ASTM E-28 | 150 | °C |
| cloud point | 石蜡 | | 66 | °C |
| Vicat softening temperature | | ASTMD1525 | 61.0 | °C |
| Vicat softening temperature | | ISO306 | 61.0 | °C |
| Peak melting temperature | | ASTMD3418 | 86.0 | °C |
| Melting temperature (DSC) | | ISO3146 | 86.0 | °C |
| vicat softening point | | ASTM D1525/ISO R306 | 61 | ℃（℉） |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Temperature | | | <230 | °C |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D-792 | 0.941 | g/cm³ |
| Melt index | 190℃/2.16kg | ASTM D-1238 | 8 | g/10min |
| VA content | | | 18 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.