Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | ISO294-4 | 0.70到1.3 | % |
| Shrinkage rate | MD | ISO294-4 | 0.10到0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | 断裂,23°C | ISO527-2 | 80.0 | Mpa |
| Tensile strain | 断裂,23°C | ISO527-2 | 2.8 | % |
| Tensile modulus | 23°C | ISO527-2 | 5800 | Mpa |
| Bending modulus | 23°C | ISO178 | 4200 | Mpa |
| Bending stress | 23°C | ISO178 | 110 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 150 | °C |
| Melting temperature | | ISO11357-3 | 225 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+13 | ohms |
| Volume resistivity | | IEC60093 | 1E+14 | ohms·cm |
| Dielectric strength | 2.00mm | IEC60243-1 | 23 | KV/mm |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| MeltViscosity | 260°C | ISO11443 | 185 | Pa·s |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.