Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Flow coefficient | 200℃，5kg | ISO 1133 | 2.7 | cm3/10min |
| Flow coefficient | 220℃，10kg | ISO 1133 | 30 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | 50 mm/min | ISO 527 | 46 | Mpa |
| Elongation rate | 50 mm/min | ISO 527 | 20 | % |
| bending strength | 2mm/min | ISO 178 | 70 | Mpa |
| Flexural elasticity | 2 mm/min | ISO 178 | 2.4 | GPa |
| IZOD impact strength | 4mm/23℃ | ISO 180 | 15 | kJ/m² |
| Charpy impact strength | 4mm/23℃ | ISO 179 | 17 | kJ/m3 |
| hardness | | ASTM D785 | 116 | R |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| softening point | 10N，50℃/hr | ISO 306 | 105 | °C |
| Hot deformation temperature | 1.8MPa annealed | ISO 75-2 | 100 | °C |
| Hot deformation temperature | 1.8MPa unannealed | ISO 75-2 | 85 | °C |
| Combustion rate | 1.5mm | File No.E194560
UL&C-UL | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.