Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 0.85 | g/10min |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTMD1525 | 106 | °C |
| Melting temperature (DSC) | | 内部方法 | 123 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film thickness - tested | | | 25 | µm |
| Membrane puncture strength | | 内部方法 | 5.76 | J |
| Membrane piercing force | | 内部方法 | 64.5 | N |
| Membrane puncture resistance | | 内部方法 | 28.3 | J/cm³ |
| Membrane strength | MD | ASTMD882 | 98.5 | J/cm³ |
| Membrane strength | TD | ASTMD882 | 98.5 | J/cm³ |
| Secant modulus | 1%正割,MD | ASTMD882 | 272 | Mpa |
| Secant modulus | 2%正割,MD | ASTMD882 | 231 | Mpa |
| Secant modulus | 1%正割,TD | ASTMD882 | 309 | Mpa |
| Secant modulus | 2%正割,TD | ASTMD882 | 256 | Mpa |
| Tensile strength | MD:屈服 | ASTMD882 | 11.9 | Mpa |
| Tensile strength | TD:屈服 | ASTMD882 | 12.4 | Mpa |
| Tensile strength | MD:断裂 | ASTMD882 | 43.6 | Mpa |
| Tensile strength | TD:断裂 | ASTMD882 | 36.0 | Mpa |
| elongation | MD:断裂 | ASTMD882 | 480 | % |
| elongation | TD:断裂 | ASTMD882 | 620 | % |
| Falling hammer impact | | ASTMD1709A | 540 | g |
| Elmondov tear strength | MD | ASTMD1922 | 260 | g |
| Elmondov tear strength | TD | ASTMD1922 | 670 | g |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| gloss | 45° | ASTMD2457 | 33 | |
| Haze | | ASTMD1003 | 20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.