Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD:3.00mm | % | 0.35 | -- |
| Shrinkage rate | TD:3.00mm | % | 0.70 | -- |
| Water absorption rate | 24hr,3.18mm | % | 0.26 | -- |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation | 断裂 | % | 4.0 | 6.0 |
| Bending modulus | | MPa | 8200 | 6300 |
| bending strength | | MPa | 211 | 181 |
| compressive strength | | MPa | 147 | -- |
| Tensile strength | | MPa | 143 | 112 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 4.6E-05 | -- |
| Hot deformation temperature | 1.8MPa,未退火 | °C | 179 | -- |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric constant | 1MHz | | -- | 3.60 |
| Arc resistance | | sec | -- | 60.0 |
| Volume resistivity | | ohms·cm | -- | |
| Dissipation factor | 1MHz | | -- | |
| Dielectric strength | | kV/mm | -- | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R级 | | 121 | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices