PC Makrolon® 2405 BK COVESTRO SHANGHAI

361

Properties:
Low viscosity
Usages:
Electrical field
Electronic field
Industrial applications
Automotive sector
currency
currency
Certificates:
UL
Compare
View Prices

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:2.00mm3	ISO294-4	0.70	%
	Shrinkage rate	MD:2.00mm3	ISO294-4	0.65	%
		Shrinkage rate	TD	ISO2577	0.50to0.70	%
		Shrinkage rate	Shrinkage rate	MD	ISO2577	0.50to0.70	%
Water absorption rate	饱和,23°C	ISO62	0.30	%
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO62	0.12	%
Melt mass flow rate	300°C/1.2kg	ISO1133	20	g/10min
Melt volume flow rate	300°C/1.2kg	ISO1133	19.0	cm3/10min
Density/specific gravity	23°C	ISO1183	1.20	g/cm³
Apparent density 2		ISO60	0.66	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Nominal tensile fracture strain	23°C	ISO527-2/50	>50	%
TensileCreepModule	1hr	ISO899-1	2200	Mpa
Tensile stress	屈服,23°C	ISO527-2/50	65.0	Mpa
Tensile stress	Tensile stress	断裂,23°C	ISO527-2/50	65.0	Mpa
Tensile strain	屈服,23°C	ISO527-2/50	6.0	%
Tensile strain	Tensile strain	断裂,23°C	ISO527-2/50	130	%
Tensile creep modulus	1000hr	ISO899-1	1900	Mpa
Tensile modulus	23°C	ISO527-2/1	2400	Mpa
Bending stress 4	3.5%Strain,23°C	ISO178	73.0	Mpa
Bending stress 4	Bending stress 4	23°C	ISO178	97.0	Mpa
Bending modulus 4	23°C	ISO178	2350	Mpa
Bending strain 5	23°C	ISO178	7.1	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Glass transition temperature 8		ISO11357-2	144	°C
Thermal conductivity coefficient 9	23°C	ISO8302	0.20	W/m/K
Hot deformation temperature	0.45MPa,未退火	ISO75-2/B	137	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,未退火	ISO75-2/A	124	°C
RTIElec	1.5mm	UL746	125	°C
Evolution Calendar intelligent importer	1.5mm	UL746	115	°C
RTIStr	1.5mm	UL746	125	°C
Linear coefficient of thermal expansion	MD：23到55°C	ISO11359-2	6.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C
Vicat softening temperature	--	ISO306/B50	145	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/B120	146	°C
BallPressure Test	136°C	IEC60695-10-2	Pass

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	23°C,1.00mm	IEC60243-1	34	KV/mm
Dissipation factor	23°C,100Hz	IEC60250	5E-04
Dissipation factor	Dissipation factor	23°C,1MHz	IEC60250	9E-03
Relative permittivity	23°C,100Hz	IEC60250	3.10
Relative permittivity	Relative permittivity	23°C,1MHz	IEC60250	3.00
Leakage Trace Index	解决方案A	IEC60112	250	V
Leakage Trace Index	Leakage Trace Index	解决方案B	IEC60112	125	V
Surface resistivity		IEC60093	1E+16	ohms
Volume resistivity	23°C	IEC60093	1E+16	ohms·cm

film	Test Condition	Test Method	Test Result	Unit
WaterVaporTransmission Rate	23°C,85%RH,100µm	ISO15106-1	15	g/m²/24hr
GasPermeation	CarbonDioxide:23°C,25.4µm	ISO2556	18900	cm³/m²/bar/24hr
	GasPermeation	CarbonDioxide:23°C,100.0µm	ISO2556	4000	cm³/m²/bar/24hr
		GasPermeation	Nitrogen:23°C,25.4µm	ISO2556	630	cm³/m²/bar/24hr
			GasPermeation	Nitrogen:23°C,100.0µm	ISO2556	130	cm³/m²/bar/24hr
				GasPermeation	Oxygen:23°C,25.4µm	ISO2556	3150	cm³/m²/bar/24hr
				GasPermeation	GasPermeation	Oxygen:23°C,100.0µm	ISO2556	700	cm³/m²/bar/24hr

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam gap 6	-30°C,完全断裂	ISO7391	14	kJ/m²
Impact strength of simply supported beam gap 6	Impact strength of simply supported beam gap 6	23°C,局部断裂	ISO7391	65	kJ/m²
Suspended wall beam gap impact strength 7	-30°C,完全断裂	ISO7391	15	kJ/m²
Suspended wall beam gap impact strength 7	Suspended wall beam gap impact strength 7	23°C,局部断裂	ISO7391	65	kJ/m²
Multi axis Instrumented Peak Impact Force	-30°C	ISO6603-2	6000	N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO6603-2	5100	N
Impact strength of simply supported beam without notch	-60°C	ISO179/1eU	NoBreak
	Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak
Multi axis Instrumented Impact Energy	-30°C	ISO6603-2	65.0	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO6603-2	55.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	115	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive Index11		ISO489	1.585
transmissivity	3000µm	ISO13468-2	88.0	%
	transmissivity	4000µm	ISO13468-2	87.0	%
		transmissivity	1000µm	ISO13468-2	89.0	%
		transmissivity	transmissivity	2000µm	ISO13468-2	89.0	%
Haze	3000µm	ISO14782	<0.80	%

flammability	Test Condition	Test Method	Test Result	Unit
ApplicationofFlamefromSmallBurner MethodKandF	2.00mm	DIN53438-1,-3	K1,F1
Burning rate - US-FMVSS	>1.00mm	ISO3795	passed
FlashIgnitionTemperature		ASTMD1929	480	°C
Needle flame test	MethodF:1.50mm	IEC60695-11-5	1.0	min
	Needle flame test	MethodF:2.00mm	IEC60695-11-5	2.0	min
		Needle flame test	MethodF:3.00mm	IEC60695-11-5	2.0	min
			Needle flame test	MethodK:1.50mm	IEC60695-11-5	0.1	min
				Needle flame test	MethodK:2.00mm	IEC60695-11-5	0.1	min
				Needle flame test	Needle flame test	MethodK:3.00mm	IEC60695-11-5	0.2	min
Extreme Oxygen Index 10		ISO4589-2	27	%
SelfIgnition		ASTMD1929	550	°C
UL flame retardant rating	2.7mm	UL94	HB
	UL flame retardant rating	0.36mm	UL94	V-2
	UL flame retardant rating	UL flame retardant rating	0.75mm	UL94	V-2
Burning wire flammability index	0.75mm	IEC60695-2-12	850	°C
	Burning wire flammability index	1.5mm	IEC60695-2-12	875	°C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC60695-2-12	930	°C
Hot filament ignition temperature	0.75mm	IEC60695-2-13	875	°C
	Hot filament ignition temperature	1.0mm	IEC60695-2-13	875	°C
		Hot filament ignition temperature	1.5mm	IEC60695-2-13	875	°C
		Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC60695-2-13	875	°C

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ISO Shortcut			ISO7391-PC,MR,(,,)-18-9
ElectrolyticalCorrosion	23°C	IEC60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PC Makrolon® 2405 BK COVESTRO SHANGHAI

Technical Data Sheet