Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ASTMD1505 | 0.920 | g/cm³ |
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 2.0 | g/10min |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Brittle temperature | | ASTMD746 | -70.0 | °C |
| Vicat softening temperature | | ASTMD1525 | 93.0 | °C |
| Melting temperature | | | 122 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film thickness - tested | | | 38 | µm |
| Secant modulus | 1%正割,MD:38µm,吹塑薄膜 | ASTMD882 | 147 | Mpa |
| Secant modulus | 1%正割,TD:38µm,吹塑薄膜 | ASTMD882 | 206 | Mpa |
| Tensile strength | MD:屈服,38µm,吹塑薄膜 | ASTMD882 | 9.81 | Mpa |
| Tensile strength | TD:屈服,38µm,吹塑薄膜 | ASTMD882 | 10.8 | Mpa |
| Tensile strength | MD:断裂,38µm,吹塑薄膜 | ASTMD882 | 35.3 | Mpa |
| Tensile strength | TD:断裂,38µm,吹塑薄膜 | ASTMD882 | 27.5 | Mpa |
| elongation | MD:断裂,38µm,吹塑薄膜 | ASTMD882 | 600 | % |
| elongation | TD:断裂,38µm,吹塑薄膜 | ASTMD882 | 800 | % |
| Falling hammer impact | 38µm,吹塑薄膜 | ASTMD1709 | 120 | g |
| Elmondov tear strength | MD:38µm,吹塑薄膜 | ASTMD1922 | 61 | g |
| Elmondov tear strength | TD:38µm,吹塑薄膜 | ASTMD1922 | 650 | g |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| gloss | 45°,38.0µm,吹塑薄膜 | ASTMD2457 | 47 | |
| transparency | | ASTMD1746 | 53.0 | |
| Haze | 38.0µm,吹塑薄膜 | ASTMD1003 | 24 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.