POM Delrin® 500AL DUPONT USA
65
- Properties:Dimensional stabilityFatigue resistanceHigh impact resistance
- Usages:Household appliancesBottle capIndustrial applicationsAutomotive sectorElectronic fieldElectrical field
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.7 | % |
| MD | ISO294-4 | 1.8 | % | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.30 | % |
| Melt Volume-Flow Rate (MVR) | 190°C/2.16kg | ISO1133 | 12.0 | cm3/10min |
| MediumDensity | 1.18 | g/cm³ | ||
| Melt mass flow rate | ISO1133 | 14 | g/10min | |
| density | ISO1183 | 1.39 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 6.0 | kJ/m² |
| 23°C | ISO179/1eA | 7.0 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 5.0 | kJ/m² |
| 23°C | ISO180/1A | 6.0 | kJ/m² | |
| TensileCreepModule | 1hr | ISO899-1 | 2400 | Mpa |
| Nominal tensile fracture strain | ISO527-2 | 23 | % | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 130 | kJ/m² |
| 23°C | ISO179/1eU | 160 | kJ/m² | |
| Tensile creep modulus | 1000hr | ISO899-1 | 1600 | Mpa |
| Tensile modulus | ISO527-2 | 3000 | Mpa | |
| tensile strength | 屈服 | ISO527-2 | 66.0 | Mpa |
| elongation | 屈服 | ISO527-2 | 11 | % |
| Bending modulus | ISO178 | 2800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ISO11357-3 | 178 | °C | |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 164 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 97.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| AnnealingTemperature | 160 | °C | ||
| AnnealingTime-Optional | 30.0 | min/mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.8mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS flammability | FMVSS302 | B | ||
| Burning rate | 1.00mm | ISO3795 | 28 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission | VDA275 | <8.00 | mg/kg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.