Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| 23℃ | | % | 0.14到1.0 | |
| 23℃,24hr | | % | 0.30到0.51 | |
| Balance, 23 ℃, 50% RH | | % | 0.21到1.2 | |
| Lateral flow: 23 ℃ | | mm/mm | 119.4E-3到0.254 | |
| 23℃,24hr | | % | 0.12到0.30 | |
| Flow: 23 ℃ | | mm/mm | 48.3E-3到129.5E-3 | |
| 23℃ | | g/cm³ | 1.29到1.78 | |
| -- | | | 1.33到1.73 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| shear strength | 23℃ | MPa | 88.28到107.59 | |
| 23℃ | | MPa | 8827.59到14482.76 | |
| Yield, 23 ℃ | | MPa | 102.76到362.76 | |
| Poisson's ratio | 23℃ | | 0.41 | |
| compressive strength | 23℃ | MPa | 142.76到196.55 | |
| Yield, 23 ℃ | | % | 1.4到2.5 | |
| 23℃ | | MPa | 5137.93到18620.69 | |
| 23℃ | | MPa | 126.21到364.14 | |
| Fracture, 23 ℃ | | % | 1.5到3.1 | |
| Fracture, 23 ℃ | | % | 1.0到2.5 | |
| Tensile modulus | 摩擦系数 | | 0.15到0.52 | |
| Yield, 23 ℃ | | MPa | 68.97到250.34 | |
| Fracture, 23 ℃ | | MPa | 131.72到400.0 | |
| 23℃ | | MPa | 5337.93到17586.21 | |
| 23℃ | | MPa | 5200.0到18344.83 | |
| Fracture, 23 ℃ | | MPa | 162.76到199.31 | |
| Yield, 23 ℃ | | % | 1.5到2.6 | |
| 23℃ | | MPa | 88.28到260.0 | |
| Yield, 23 ℃ | | MPa | 12.62到270.34 | |
| Fracture, 23 ℃ | | MPa | 108.28到262.76 | |
| 23℃ | | MPa | 137.93到392.41 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| flow | | mm/mm/°C | 195.6E-5到25.4E-5 | |
| -- | | °C | 310到312 | |
| Vicat softening temperature | | °C | 258到313 | |
| 8.0Mpa, unannealed | | °C | 165到230 | |
| 1.8MPa, unannealed | | °C | 247到292 | |
| 0.45MPa, annealed | | °C | 296到320 | |
| 0.45MPa, unannealed | | °C | 275到308 | |
| RTI | | °C | 119到150 | |
| Continuous use temperature | | °C | 140到186 | |
| transverse | | mm/mm/°C | 68.6E-5到127.0E-5 | |
| 1.8MPa, annealed | | °C | 283到300 | |
| transverse | | mm/mm/°C | 63.5E-5到177.8E-5 | |
| 0.45MPa, unannealed | | °C | 273到312 | |
| Evolution Calendar intelligent importer | | °C | 118到150 | |
| RTIElec | | °C | 140到150 | |
| flow | | mm/mm/°C | 38.1E-5到50.8E-5 | |
| 1.8MPa, unannealed | | °C | 249到304 | |
| flow | | mm/mm/°C | 185.4E-5到25.4E-5 | |
| -- | | °C | 299到315 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Compared to the anti leakage trace index | CTI | V | 548到600 | |
| -- | | ohms | 1.0E+5到2.5E+16 | |
| Leakage Trace Index | | V | 593到600 | |
| 23℃ | | ohms·cm | 1.0E+3到2.5E+15 | |
| 23℃ | | V/mil | 420到1100 | |
| 23℃ | | ohms·cm | 1.0E+15到2.6E+16 | |
| 23℃ | | | 4.9E-3到0.015 | |
| 23℃ | | | 3.66到5.52 | |
| 23℃ | | | 4.0E-3到0.017 | |
| -- | | ohms | 1.0E+2到2.5E+15 | |
| 23℃ | | V/mil | 450到590 | |
| 23℃ | | | 3.66 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| 23℃ | | J | 0.78到2.04 | |
| 23℃ | | kJ/m² | 0.556到3.158 | |
| 23℃ | | kJ/m² | 4.365到15.786 | |
| 23℃ | | J/m | 0.066到0.351 | |
| 23℃ | | J/m | 0.008到0.042 | |
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 4.178到19.964 | |
| 23℃ | | N.m | 138.05到788.50 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | 23℃ | | 125 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Extreme Oxygen Index | | % | 23到25 | |
| Burning wire flammability index | | °C | 743到960 | |
| Hot filament ignition temperature | | °C | 721到926 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.