ABS TAIRILAC® AX4000 FCFC TAIWAN
1969
- Properties:heat-resistingHeat resistance
- Usages:ShellAutomotive External PartsElectrical appliancesHousehold appliancesAutomotive partsElectrical appliancesHair dryer
- Certificates:ULMSDSTDSProcessingMSDSULRoHSRoHSSVHCEnvironmental
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.05 | g/cm³ | |
| 23°C | ISO1183 | 1.05 | g/cm³ | |
| 220°C/10.0kg | ASTMD1238 | 10 | g/10min | |
| 220°C/10.0kg | ISO1133 | 10 | g/10min | |
| Shrinkage rate | MD | 内部方法 | 0.40to0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | 屈服,23°C | ISO527-2 | 43.0 | Mpa |
| Bending modulus | 23°C | ASTMD790 | 2550 | Mpa |
| 23°C | ISO178 | 2550 | Mpa | |
| bending strength | 23°C | ASTMD790 | 76.0 | Mpa |
| Bending stress | 23°C | ISO178 | 76.0 | Mpa |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ISO180 | 170 | J/m |
| 23°C,6.35mm | ASTMD256 | 170 | J/m | |
| Tensile strength | 23°C | ASTMD638 | 43.1 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火,12.7mm | ASTMD648 | 98.0 | °C |
| 1.8MPa,Unannealed,12.7mm | ISO75-2/A | 98.0 | °C | |
| 1.8MPa,Annealed | ASTMD648 | 108 | °C | |
| 1.8MPa,退火 | ISO75-2/A | 108 | °C | |
| Vicat softening temperature | ASTMD15253 | 113 | °C | |
| ISO306/A | 113 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.