Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 饱和,23°C | ISO62 | 1.7 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.35 | % |
| Density/specific gravity | | ISO1183 | 1.07 | g/cm³ |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 25.0 | cm3/10min |
| Shrinkage rate | | ISO294-4 | 0.50to0.90 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2 | 2400 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2 | 51.0 | Mpa |
| Tensile strain | 屈服,23°C | ISO527-2 | 3.3 | % |
| TensileCreepModule | 1hr | ISO899-1 | 2200 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 1650 | Mpa |
| Bending stress | | ISO178 | 75.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature 2 | 0.45MPa,Annealed | ISO75-2/B | 101 | °C |
| Hot deformation temperature 2 | 1.8MPa,退火 | ISO75-2/A | 96.0 | °C |
| Vicat softening temperature | -- | ISO306/A50 | 105 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 97.0 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 8.0E-5to1.1E-4 | cm/cm/°C |
| thermal conductivity | | DIN52612 | 0.17 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+13 | ohms |
| Volume resistivity | | IEC60093 | 1E+14 | ohms·cm |
| Dielectric constant | 100Hz | IEC60250 | 3.40 | |
| Dissipation factor | 100Hz | IEC60250 | 0.010 | |
| Dissipation factor | 1MHz | IEC60250 | 0.025 | |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Elongation MD | 断裂 | ISO527-3 | 8.0 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 3.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 12 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180/A | 4.0 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/A | 11 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | | ISO2039-1 | 90.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.