PA66 POLIMID STAT A A EM4 POLIBLEND ITALY
234
- Certificates:MSDS
CompareTechnical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.05 | ||
| Molding shrinkage rate | ASTM D955 | 1.7－2.1 | % | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 0.7－0.8 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 8.0 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 1900 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 55 | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 80 | % | |
| Bending modulus | ASTM D790/ISO 178 | 1900 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 80 | % | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 65 | kg·cm/cm(J/M)ft·lb/in | |
| Charpy impact strength | ASTM D256/ISO 179 | 65 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 不可断裂 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| melting point | 260 | ℃（℉） | ||
| vicat softening point | ASTM D1525/ISO R306 | 248 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D257/IEC 60093 | 10*14 | Ω.cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.