Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD：3.20mm | ASTMD955 | 0.50 | % |
| Shrinkage rate | TD:3.20mm | ISO2577 | 0.50 | % |
| Shrinkage rate | MD:3.20mm | ISO2577 | 0.40 | % |
| Density/specific gravity | | ASTMD792 | 1.13 | g/cm³ |
| Density/specific gravity | | ISO1183 | 1.13 | g/cm³ |
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 19 | g/10min |
| Melt mass flow rate | 220°C/10.0kg | ISO1133 | 19 | g/10min |
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus 2 | | ASTMD638 | 2400 | Mpa |
| Tensile modulus | | ISO527-2/50 | 2600 | Mpa |
| Tensile strength 2 | 屈服 | ASTMD638 | 47.0 | Mpa |
| Tensile stress | 屈服 | ISO527-2/50 | 53.0 | Mpa |
| Tensile strength 2 | 断裂 | ASTMD638 | 29.0 | Mpa |
| Tensile stress | 断裂 | ISO527-2/50 | 38.0 | Mpa |
| Elongation rate 2 | 断裂 | ASTMD638 | 15 | % |
| Tensile strain | 断裂 | ISO527-2/50 | 20 | % |
| Bending modulus 3 | | ASTMD790 | 2500 | Mpa |
| Bending modulus 4 | | ISO178 | 2600 | Mpa |
| Bending strength 3 | | ASTMD790 | 69.0 | Mpa |
| Bending stress 4 | | ISO178 | 80.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 93.0 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 88.0 | °C |
| Hot deformation temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 84.0 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 76.0 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 95.096.0 | °C |
| Vicat softening temperature | -- | ISO306/B120 | 98.099.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 10 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTMD256 | 120 | J/m |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 88 | J/m |
| Suspended wall beam gap impact strength 5 | 23°C | ISO180/1A | 10 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R级 | ISO2039-2 | 116 | |
| PencilHardness6 | | JISK5401 | H | |
| Rockwell hardness | R级 | ASTMD785 | 114 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.